| Loss On Ignition (%) | 2.5 |
|---|---|
| Specific Gravity G/cm3 | 4.4 |
| D97 (μm) | 22 |
| D50 (μm) | 8.5 |
| Oil Absorption (g/100g) | 12~14 |
| Moisture(%) | 0.2 |
|---|---|
| Specific Gravity(g/cm3) | 4.4 |
| Loss On Ignition(%) | 1 |
| CaO Content (Wt %) | 0.3 |
| Whiteness(%) | 88 |
| D50 (μm) | 0.7 |
|---|---|
| Whiteness (%) | 98.8 |
| BaSO4 Content (%) | 98.8 |
| Specific Gravity G/cm3 | 4.4 |
| Oil Absorption G/100g | 15~18 |
| Moisture(%) | 0.2 |
|---|---|
| Specific Gravity(g/cm3) | 4.4 |
| Loss On Ignition(%) | 1 |
| CaO Content (Wt %) | 0.3 |
| Whiteness(%) | 88 |
| Moisture(%) | 0.2 |
|---|---|
| Specific Gravity(g/cm3) | 4.4 |
| Loss On Ignition(%) | 1 |
| CaO Content (Wt %) | 0.3 |
| Whiteness(%) | 88 |
| Apperance Outlook | White Powder |
|---|---|
| Mesh | 2000 |
| BaSO4 Content (%) | 95 |
| Whiteness (%) | 93 |
| Moisture (%) | 0.2-0.3 |
| D50 (μm) | 2.06 |
|---|---|
| D97 (μm) | 5.64 |
| Whiteness (%) | 93.5 |
| Moisture (%) | 0.25 |
| Oil Absorption G/100g | 13-16 |
| Apperance Show | Dark Powder |
|---|---|
| D50 (μm) | 7.6 |
| D97 (μm) | 21 |
| Content (%) | 94 |
| Whiteness (%) | 50 |
| D50 (μm) | 0.7 |
|---|---|
| Whiteness (%) | 98.8 |
| BaSO4 Content (%) | 98.8 |
| Specific Gravity G/cm3 | 4.4 |
| Oil Absorption G/100g | 15~18 |
| D50 (μm) | 0.7 |
|---|---|
| Whiteness (%) | 98.8 |
| BaSO4 Content (%) | 98.8 |
| Specific Gravity G/cm3 | 4.4 |
| Oil Absorption G/100g | 15~18 |